Studying the "induction welding" process applied to thermoplastic-matrix composites

di Flavio Caretto - ENEA, Technical Unit for Brindisi Material Technologies

In recent years the number of applications requiring the use of thermoplastic-matrix composites has increased enormously and so has the emphasis on the assembling techniques of these materials. In particular, alternatives to traditional mechanical fasteners or bonding are of great interest to industry. The present work is a study of a welding process, called "induction welding", of a composite material made of polyphenylene sulfide reinforced with woven carbon fiber. Process parameters such as temperature, pressure, residence time and presence of susceptor elements at the weld interface were considered. The number of tests to be conducted has been optimized by using DOE (Design of Experiment) techniques. The quality of the weld was evaluated with ultrasound and non-destructive mechanical testing

Studio del processo di saldatura induction welding applicato a compositi a matrice termoplastica

Negli ultimi anni il numero di applicazioni che prevedono l’utilizzo di compositi a matrice termoplastica è aumentato enormemente e di conseguenza anche l’attenzione verso le tecniche di assemblaggio di questi materiali. In particolare, sistemi alternativi alle classiche giunzioni meccaniche o all’incollaggio sono di grosso interesse per l’industria. Il presente lavoro consiste nello studio di un processo di saldatura, denominato “induction welding” di un materiale composito costituito da polifenilensolfuro rinforzato con tessuti in fibra di carbonio. Parametri di processo quali temperatura, pressione, tempo di residenza e presenza di elementi suscettori all’interfaccia di saldatura sono stati considerati. Il numero delle prove da effettuare è stato ottimizzato per mezzo di tecniche DOE (Design of Experiment). La qualità della saldatura è stata valutata con controlli non distruttivi agli ultrasuoni e test meccanici